PENGARUH RAPAT ARUS ANODIZING TERHADAP NILAI KEKERASAN PADA PLAT ALUMINIUM PADUAN AA SERI 2024-T3

Fajar Nugroho

Submitted : 2017-09-14, Published : .

Abstract

Aluminum alloy AA 2024-T3 is widely applied in the aircraft industry because it has good mechanical properties such as; light weight, good conductivity and the corrosion resistance. However Aluminium 2024-T3 susceptible to wearing. One method to improve the wear resistance o f AA 2024-T3 is the anodizing process. The aims of this research to study the effect of current density and anodizing time against the hardness of aluminum alloy AA 2024-T3. The process of anodizing was carried out using 10 percent sulfuric acid solution with the current density of 1.5 Ampere per decimeters square, 3.0 Ampere per decimeters square and 4.5 Ampere per decimeters square with immersion times of 30, 40, 50 and 60 minutes. Furthermore, the surface hardness was measured by using the Vickers hardness test method. As the supporting data the composition of the test conducted, testing the microstructure, and vickers hardness test. This study shows that the surface hardness of aluminum alloy AA 2024-T3 is influenced by the current density and anodizing time with varying values. Its shows that higher current density o f the anodizing caused optimal time tends to be short. The longer anodising time it will produce greater layer of aluminum oxide.

Keywords

aluminium alloy AA 2024-T3, anodizing, current density, time, hardness

References

ASM Handbook, 1992, Corrosion, Metal Handbook, Vol.13.

ASTM, 2003, Metal Test Methods and Analitycal Procedurs, Anual Book of ASTM Standard, sc.3 Vol 03.01,E647-00, pp.615-657, Bar Harbor Drive Weat Conshohocken.

Apachitei, L.EF., Apachitei, I., Duszczyk, 2006, Thermal Effects Associated with Hard Anodizing of Cast Aluminum Alloys, Journal of Aplied Electrochemistry, Vol. 36, pp. 481-486.

Bardal, E., 2003, Corrosion and Protection, Springer-Verlag London, pp. 256

Callister, W.D., 2007, Material Science and Engineering an Introduction”, 7th edition, John Willey.

Canning, W., 1970, Canning HandBookon Elektroplating, 2nd edition, pp. 695-706

Choi, J., 2003, Fabrication of Monodomain Porous Alumina Using Nanoimprint Lithography and Its Application”s, desertation, Martin-Luther-Universit'at HalleWittenberg.

Fontana, M.G., 1986, Corrosion Engineering, McGraw-Hill, 3th edition, New York.

Hatch, E.J., 1984, Aluminum Properties and Physical Metallurgy, Ohio, American Society for Metal.

Jones, D.A., 1991, Principle and Prevention of Corrosion, Mc. Millan Publishing Company, New York.

Mandal, N.R., 2005, Aluminum Welding, New Delhi, Narosa Publishing House.

Masruri, D., 2010, Pengaruh Variasi Konsentrasi Larutan Asam Sulfat dan Rapat Arus Terhadap Kekerasan, Struktur Mikro, dan Ketahanan Korosi Hasil Proses anodisasi Aluminium, Thesis, Universitas Gadjah Mada

Mukhurov, N.I., Zhvayi, S.P., Terekhov, S.N., 2008, Influence of Electrolyte Composition on Photoluminescent Properties o f anodic Aluminum Oxide, Journal of Aplied Spectroscopy, Vol.75, pp. 214-217

Nugroho,F., 2014, Pengaruh Rapat Kuat Arus dan Waktu Anodizing Terhadap Laju Keausan Plat Aluminium Paduan AA 2024 T3, Jurnal Foundry, Vol.4

Pooladi, R., Rezai, H., Aezami, M., Sayyar, M.R., 2009, Fabrication o f Anodic Aluminum Oxide Nanotemplate and Investigation o f Their Anodization Parameters, Transaction of Indian Institute of Metals, Vol. 62, Issue 3, pp. 241-244.

Polmear, I.J., 1981, Light Alloy, 3 th edition Arnold, London

Sadeler, R., Atasoy, S., Arici, A., and Totik, Y., 2009, The Fretting Fatigue of Comercial Hard Anodized Aluminum Alloy, ASM International, Journal of Material Engineering and Performance, Vol 19., pp. 1280-1283.

Shulgov, V., Ignasheve, E., Gurskaja, E., 2007,Correlation Between Formation Condition and Breakdown Voltage o f Anodic Films on Aluminum, Michrochimica Acta, Springer-Verlag, pp. 147-150.

Soekrisno,R., 2012, Optimalisasi Temperatur Hard Anodizing terhadap Ketahanan Aus, Kekerasan serta Ketebalan Lapisan Oksida Aluminium Paduan, Hasil Penelitian Hibah Prodi S2 Teknik Mesin JTMI FT UGM.

Staley, J.T. and Lege, D.J., 1993, Advanced in Aluminum Alloy Product For Struktural Application in Transportation, Journal De Physique III, 3, 197-190.

Trethewey, K.R., & Chamberlain, J., Korosi Untuk Mahasiswa dan Rekayasa, PT.Gramedia Pustaka Utama, Jakarta.

Vrublevsky, I., Parkoun, V., Sokol, V., Schreckenbach, J., Goedel, W.A., 2007, Dissolution Behaviour of Anodic Oxide Film Formed in Sulfanic Acid on Aluminum, Michrochimica Acta, Springer-Verlag, pp. 173-179.

http://dx.doi.org/10.28989/angkasa.v7i2.147

Article Metrics

Abstract view: 1635 times
Download     : 864   times

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.

Refbacks

  • There are currently no refbacks.